Theses and Dissertations
Permanent URI for this collection
Browse
Browsing Theses and Dissertations by Subject "back-contact"
Now showing 1 - 1 of 1
Results Per Page
Sort Options
Item Open Access Performance and metastability of CdTe solar cells with a Te back-contact buffer layer(Colorado State University. Libraries, 2017) Moore, Andrew, author; Sites, James, advisor; Krueger, David, committee member; de la Venta, Jose, committee member; Sampath, W. S., committee memberThin-film CdTe photovoltaics are quickly maturing into a viable clean-energy solution through demonstration of competitive costs and performance stability with existing energy sources. Over the last half decade, CdTe solar technology has achieved major gains in performance; however, there are still aspects that can be improved to progress toward their theoretical maximum efficiency. Perhaps equally valuable as high photovoltaic efficiency and a low levelized cost of energy, is device reliability. Understanding the root causes for changes in performance is essential for accomplishing long-term stability. One area for potential performance enhancement is the back contact of the CdTe device. This research incorporated a thin-film Te-buffer layer into the contact structure, between the CdTe and contact metal. The device performance and characteristics of many different back contact configurations were rigorously studied. CdTe solar cells fabricated with the Te-buffer contact showed short-circuit current densities and open-circuit voltages that were on par with the traditional back-contacts used at CSU. However, the Te-buffer contact typically produced ~2% larger fill-factors on average, leading to greater conversation efficiency. Furthermore, using the Te buffer allowed for incorporation of ~50% less Cu, which is used for p-type doping but is also known to decrease lifetime and stability. This resulted in an additional ~3% fill-factor gain with no change in other parameters compared to the standard-Cu treated device. In order to better understand the physical mechanisms of the Te-buffer contact, electrical and material properties of the Te layer were extracted and used to construct a simple energy band diagram. The Te layer was found to be highly p-type (>1018 cm-3) and possess a positive valence-band offset of 0.35-0.40 eV with CdTe. An existing simulation model incorporating the Te-layer properties was implemented and validated by comparing simulated results of CdTe device performance to experimental values. The Te layer improves performance is attributed to a reduction in the downward energy band bending between the CdTe and typical contact metals. The stability, or rather the metastability, of CdTe solar cells was also studied with a focus on the Te back contact. A metastable device has a series of quasi-stable local energy-minimuma which the device may transition among. This work primarily focused on changes, both beneficial and detrimental, caused by diffusion and drift of atoms in the CdTe lattice. As atoms moved and/or became ionized their defect states were shifted, which resulted in changes in the CdTe doping and recombination. Changes in performance for devices in equilibrium and under stress conditions were analyzed by electrical and material characterization. Mobile impurities and mechanisms responsible for the changes were identified---primarily the migration of interstitial Cu and Cl. The stability of CdTe solar cells with different back contacts were compared. It was found that any contact that included the Te layer was almost always more stable than the traditional contact used at CSU, most likely because of less sensitivity to the impurity profiles in the CdTe. Moreover, the Te contact configuration that introduced the least amount of Cu into the CdTe was discovered to be the most stable, both in storage and under stress conditions.